| Quantity: | |
|---|---|
2mm-160mm
Grade | C | Si | Mn | P | S | Cr | Mo | V |
34CrMo4 | 0.3 - 0.37 | Max 0.40 | 0.6 - 0.9 | max 0.025 | max 0.035 | 0.9 - 1.2 | 0.15 - 0.3 | - |
42CrMo4 | 0.38 - 0.45 | Max 0.40 | 0.6 - 0.9 | max 0.025 | max 0.035 | 0.9 - 1.2 | 0.15 - 0.3 | - |
50CrMo4 | 0.46 - 0.54 | Max 0.40 | 0.5 - 0.8 | max 0.025 | max 0.035 | 0.9 - 1.2 | 0.15 - 0.3 | - |
51CrV4 | 0.47 - 0.55 | Max 0.40 | 0.7 - 1.1 | max 0.025 | max 0.025 | 0.9 - 1.2 | - | 0.1 - 0.25 |
Thikness | t ≤ 8mm | 8mm < t ≤ 20mm | 20mm < t ≤ 60mm | ||||||||||||
Grade | Re min | Rm | A min | Z min | KVb min | Re min | Rm | A min | Z min | KVb min | Re min | Rm | A min | Z min | KVb min |
N/mm2 | % | % | J | N/mm2 | % | % | J | N/mm2 | % | % | J | ||||
42CrMo4 42CrMoS4 | 900 | 1100 to 1300 | 10 | 40 | - | 750 | 1000 to 1200 | 11 | 45 | 35 | 650 | 900 to 1100 | 12 | 50 | 35 |
Thickness | 60mm < t ≤ 100mm | 100mm < t ≤ 160mm | ||||||||
Grade | Re min | Rm | A min | Z min | KVb min | Re min | Rm | A min | Z min | KVb min |
N/mm2 | % | % | J | N/mm2 | % | % | J | |||
42CrMo4 42CrMoS4 | 550 | 800 to 950 | 13 | 50 | 35 | 500 | 750 to 900 | 14 | 55 | 35 |
| EN | ASME | DIN | JIS | GB | ISO |
34CrMo4 | 4135 | 34CrMo4 | SCM435H | 35CrMo | 34CrMo4 |
42CrMo4 | 4140, 4142 | 42CrMo4 | SCM440H | 42CrMo | 42CrMo4 |
50CrMo4 | - | 50CrMo4 | - | 50CrMo | 50CrMo4 |
51CrV4 | 6150 | 50CrV4 | SUP10 | 50CrVA | 51CrV4 |
Grade | C | Si | Mn | P | S | Cr | Mo | V |
34CrMo4 | 0.3 - 0.37 | Max 0.40 | 0.6 - 0.9 | max 0.025 | max 0.035 | 0.9 - 1.2 | 0.15 - 0.3 | - |
42CrMo4 | 0.38 - 0.45 | Max 0.40 | 0.6 - 0.9 | max 0.025 | max 0.035 | 0.9 - 1.2 | 0.15 - 0.3 | - |
50CrMo4 | 0.46 - 0.54 | Max 0.40 | 0.5 - 0.8 | max 0.025 | max 0.035 | 0.9 - 1.2 | 0.15 - 0.3 | - |
51CrV4 | 0.47 - 0.55 | Max 0.40 | 0.7 - 1.1 | max 0.025 | max 0.025 | 0.9 - 1.2 | - | 0.1 - 0.25 |
Thikness | t ≤ 8mm | 8mm < t ≤ 20mm | 20mm < t ≤ 60mm | ||||||||||||
Grade | Re min | Rm | A min | Z min | KVb min | Re min | Rm | A min | Z min | KVb min | Re min | Rm | A min | Z min | KVb min |
N/mm2 | % | % | J | N/mm2 | % | % | J | N/mm2 | % | % | J | ||||
42CrMo4 42CrMoS4 | 900 | 1100 to 1300 | 10 | 40 | - | 750 | 1000 to 1200 | 11 | 45 | 35 | 650 | 900 to 1100 | 12 | 50 | 35 |
Thickness | 60mm < t ≤ 100mm | 100mm < t ≤ 160mm | ||||||||
Grade | Re min | Rm | A min | Z min | KVb min | Re min | Rm | A min | Z min | KVb min |
N/mm2 | % | % | J | N/mm2 | % | % | J | |||
42CrMo4 42CrMoS4 | 550 | 800 to 950 | 13 | 50 | 35 | 500 | 750 to 900 | 14 | 55 | 35 |
| EN | ASME | DIN | JIS | GB | ISO |
34CrMo4 | 4135 | 34CrMo4 | SCM435H | 35CrMo | 34CrMo4 |
42CrMo4 | 4140, 4142 | 42CrMo4 | SCM440H | 42CrMo | 42CrMo4 |
50CrMo4 | - | 50CrMo4 | - | 50CrMo | 50CrMo4 |
51CrV4 | 6150 | 50CrV4 | SUP10 | 50CrVA | 51CrV4 |